crosslinkable monomer meaning in Chinese

可交联单体

Influences of content of soft monomer and hard monomer , emulsifiers , initiators , self - crosslinkable monomer and protective colloid on the properties of emulsion are studied
研究软硬单体含量、乳化剂、引发剂、自交联单体、保护胶体等对聚合物乳液性能的影响。
Self - crosslinkable latex at room temperature with high elasticity is prepared when n - hydroxymethyl acrylamide is used as self - crosslinkable monomer , and poly solidum maleate is applied as protective colloid , and pre - emulsified and semi - continuous seeded emulsion polymerization is adopted
采用n -羟甲基丙烯酯胺为自交联单体，聚马来酸钠为保护胶体，采用预乳化半连续种子乳液聚合工艺，制备出高弹性室温自交联乳液。
Results show that self - crosslinkable latex at room temperature with high elasticity can be prepared when amount of butyl acrylate is 60 % , and amount of methyl methacrylate is 40 % , and mass ratio of nonionic emulsifier to anionic emulsifer is 3 : 1 , and amount of initiator is 0 . 6 % , and amount of self - crosslinkable monomer and protective colloid is 2 % and 0 . 4 % respectively
研究结果表明：当丙烯酸丁酯的质量为60 % ，甲基丙烯酸甲酯的质量为40 % ，非离子乳化剂和阴离子乳化剂的质量配比为3 : 1 ，引发剂的质量为0 . 6 % ，自交联单体的质量为2 % ，保护胶体的质量为0 . 4 %时，可以制备出高弹性自交联乳液。